Rajesh, 1) Regarding your first point, I tested the calculatePlasticity.cc in RateIndependentModel2

Dear PRISMS Team, I am currently working with PRISMS-Plasticity and PRISMS-Fatigue to calculate

Hello, everyone We have updated PRISMS-Plasticity to enable compatibility with deal.II 9.6.2. Please

Hello Kamin and Team, I went through your paper explaining the kinematic hardening. I'm working

And this is the simulated result without using the user materials constant, some cases are reasonable

Hi Gazi, It looks like you kept old Tabular Time Neumann BCs but changed time increments and total

Hi Danish, I tried the prm_UniaxialTensionTabular.prm example (in fcc/periodicBCs) with rate-

Hello Everyone, I am a beginner in the field of CPFE simulation and its aspects and recently started

Hi Gazi, I don't believe that 9.6 is compatible yet. Could you please try deal.II-v9.5.2? -

Thank you very much Chaitali, it is working now. However, I still cannot point out my mistake. The

Hi Chaitali, Thank you very much for the detailed explanation and the helpful links. I'll study

Hi Kai, Your output does not show error, but I notice that you changed the dimension size of the RVE,

Hi Itsuki, Honestly, I do not remember since completely its more than 3 years now ;). I think in my

Hi Gazi, Yes, please read our papers on PRISMS-Fatigue and watch our YouTube videos. We can help you

Hello, I want to compare experimental tensile-tensile high-cycle fatigue results for BCC metal using

Dear, Muthanna I myself do not have much experience in using DREAM.3D to generate synthetic

Dear,Raze I refer to the tutorial video, draw the orientation pole map on the output file, I get an

Hi Krzysztof, Chaitali, Thank you for checking. It seems that some definitions were indeed missing in

yes 在2025年3月18日星期二 UTC+8 18:47:04<Chaitali Patil> 写道： Hi Kai, are you running example prm file?

Hello Reza, I am trying to run some plasticity simulation with cyclic loading using PeriodicBC in

Hi Kai, You need to write two files, one representing grainIDs and other representing orientation

Hi Timothy, You actually do have the files you need to define your FIPs, it is just that they are not

Hi Danish, Chaitali, Samuel, I have successfully obtained the correct output in quadratureoutput.csv!

Hi Tanvir, Please try installation with deal-ii 9.4 or 9.5, we have to yet update the code for the

I found that this error can also be solved by removing the line "using namespace std;" from

Hi Muhammad, For rate dependent formulation, copy all files from plasticity/src/materialModels/

Thank you for the reply. As per your suggestion, I identified the problem with code compilation. Now

Thank you for the reply. I will implement the same and let you know. On Thursday, January 16, 2025 at

You can use the rate dependent model for twinning. However, the advanced twin model is implemented

The errors that occur at runtime are shown in the screenshot below. 在2024年12月19日星期四 UTC+8 14:48:16

Hi Kush, To my knowledge, this has not yet been implemented into PRISMS-Fatigue and I do not think