Dear mumax community, We are happy to announce the release of mumax 3.12, which includes a variety of

Hi, It should work. You might have to modify the build instructions slightly (ie, your version of Go

Hi, Kindly clarify whether the value we are using in place of J = vector (0, 0, ?e11) corresponds to

As the value of Aex is increasing the magnetization is going more towards x-direction . But when am

Hi, as I discussed, the current density direction is defined in the SOT implementation https://groups

Hi, Running your script briefly, it seems to complete as expected. The relax() just returns really

Hi, Have you taken a look to the examples in the mumax workshop? In particular, there are 2 examples

Thanks for the reply. It seems really tough though . How it shud be executed? Will these paper give

Hi, The default region is 0. All the cells have a region. Therefore, it is better to start by region

Hi, In that script, one thing I notice missing is that you did not set the anisotropy axis for the

Hi, When using B_ext.add(), you can apply a sinusoidal time varying term as B_ext.add(mask, -A*sin(2*

Hi, You can set GammaLL as a parameter, if you need a different one (since it is just a prefactor,

Hii, Yes, I have added the B_ext exactly in this way. Thanks Sandeep Kumar PhD (Physics) Indian

Hi Sir, I would also like to study the effect of different Ru spacer thicknesses in my Co/Ru/Co SAF

Hi, Unfortunately, mumax currently does not include the ability to do this automatically. You have to

Hi, You can find an example of a VCMA script in the mumax workshop, in particular session 4. If you

Hi, The easiest way is to simply sum them together when applying the electric current density J. For

Hi there, I would like to share a native macOS port of mumax3! I hope this will be useful to

Hi, Q1. This issue has been addressed in one of the recent posts on this mailing list: https://groups

Hi, you are right. very thanks! The CPU will indeed be a bottleneck. But the main cause is the source

Hi, I'm not particularly familiar with specifics of spin waves with i-DMI, but I have a few

HI, I recommend loading the OVF files into Python/Wolfram/Matlab and process the raw data rather than

Hi, The definition of B_eff in mumax3 does not include M, it is referring to the effective field term

Hi, I am using mumax3.10. Considering the equation B = mu_0 (H + M), I wonder how can I extract H

Hi, I am working on current-induced switching; for that, I am giving pulsed current, ie, after a

Dear MuMax3 community, I am simulating SOT-driven domain wall motion in a Pt/Co nanostrip using

Hi Sir, Thank you very much for your valuable comments regarding my implementation of the interlayer

Hi First of all, I would like to express my gratitude for taking the time to reply to my question in

Hi, Previously in mumax3, specifically for a radially symmetric one, you would need to do it as you

Hi, Unfortunately, mumax-view was designed to view magnetizations (a vector quantity), not a scalar

Hi, If you need a spiral magnetization, you can use the Helical() command. If you want a helical