Oi Altoé Que bom que funcionou :-) abraco Luiz On 24. Jun 2020, at 23:54, Rhander Altoé <rhander.

Hi, using the lastest commits, inclusionId seems to be fine and the minium shapefactor I get for

Hi Marcel, you should compute the angle by angle(mori,CSL(3,CS)) Ralf. On Wednesday, August 14, 2019

Hey Rudiger! Sorry for just now getting back to you. Your suggestion was perfect! I'll reply

Thanks, Ralf, It works Best Regards Camilo El viernes, 12 de abril de 2019, 13:44:07 (UTC-5), Ralf

Hi, If I understand correctly, you remove grains whcih touch the boundary? Probably you need to do

I was under the impression that I will always get integers since it's in a basic cubic crystal co

Thank you so much for both of your quick responses. Both of these responses were very helpful. On

Hi Matteo, can you give an example how you do it? Are you using a loop somewhere? Cheers, Rüdiger

Hi, That's okay, good to try to help. Share your knowledge to colleagues and on here as you get

Hi Andrew, the grains have a field called id which does not change after taking subsets and what is

Hi I want to plot Grain size distribution histogram in relative unit (Y-axis) or vs grain size in

Thanks very much for the help, Mr. Mainprice. I made a comparison of the values of different texture

Thanks a million Ralf, It's working perfectly. El viernes, 31 de mayo de 2013 12:55:23 UTC+1,

Hey Ralf, thank you for the response. I tried the following to extrapolate misorientation axis and

Have you tried angles = get(grains,'Euler','Kocks')? Ralf. On Tuesday, December 8,

Thank you very much for your quick answer, it really helped. This way is much easier (and smarter)

Dear Andrew, the vertices of the grain boundary are stored in the field 'V'. In a GrainSet

Hi Scarlet, it seems you Euler angles are flipped around, which causes the problem with the symmetry.

Thanks for your answer. It really helped me!