without symmetry orientation space is 360, 180, 360. Symmetry elements in hexagonal symmetry group

Thank you so much! I switched from a windows to MAC so I'm still getting used to it. My issue is

Hi Luiz! Ah ha, well let me show you what I mean by 'aggressively' reducing the seismic

Hi Matteo, for directions your will get 3 eigenvectors/values but for orientations there are 4 values

please give me your mail id Leonardo.F On Friday, September 23, 2016 at 12:29:43 PM UTC+5:30, 亓智敏

Hi, thanks for taking the time for checking my data. It's good to know that is not only me who

Dear Dr Ralf, Thank you for the prompt response. Weights of particular orientations should represent

Hello, so I am trying to retrieve two orientations from my pole figure- those of the main texture

You may try caxis(gca,[0,50]) after plotting Ralf. On Wednesday, January 6, 2016 at 5:01:53 PM UTC+1,

Thank you very much Ralf. I appreciate your reply. I am currently using the 3.5.0 version of MTEX,

Hi Ercan Çakmak, I think you should use pure MATLAB functionality to export those values to an ASCII

Hi, Thanks Ralph for taking the time of checking the data. The problem was precisely that. I can'

Dear Anwar Chaabani, please do not forget to answer my questions. I really would like to understand