Can anybody suggest if we can prepare a asme ix wps based on the test carried out as per iso 15614-1? 

On Fri, 14 Feb, 2025, 6:06 pm , <material...@googlegroups.com> wrote:
sujit kumar <sujitku...@gmail.com>: Feb 13 08:33AM +0300

Hello experts
 
Greetings for the day.
 
 
Kindly please tell me what will be the filler wire for welding of
SA182F11 to SSA268 TP446
 
 
 
 
Best regards
Sujit kumar
sridhar cn <sridha...@gmail.com>: Feb 13 11:00PM +0530

ERNiCr-3 (Inconel 82) for corrosion resistance or ERNiCrMo-3 (Inconel
625) for corrosion resistance
and extreme environments, or ER309L for general purpose could be used.
Preheating & interpass temp. control will help to minimize the risk of
cracking. PWHT might be necessary
to relieve stresses and improve the weld properties.
Sridhar.
-------------------------------------------------------------------------------------------------------------------------------------
 
 
You received this digest because you're subscribed to updates for this group. You can change your settings on the group membership page.
To unsubscribe from this group and stop receiving emails from it send an email to materials-weld...@googlegroups.com.

venkateswara reddy Desireddy

unread,
Feb 15, 2025, 3:13:31 AMFeb 15
to material...@googlegroups.com
Both codes are not identical,
Both codes having separate formats. Mechanical testings tensile and bend test same for both codes. So after testing you can write WPS for ASME and PED separate.

Regards 
D.V.Reddy

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAEJozaJHmQHhU37qEZz-L2FrKMP1JtzMw%3DJbjYTU%2BjtGZ5SCYA%40mail.gmail.com.

Deerendra Karanth

unread,
Feb 15, 2025, 1:45:36 PMFeb 15
to material...@googlegroups.com
ASME Section IX and ISO 15614-1 have overlapping but not identical requirements. You must verify that the ISO 15614-1 qualification meets ASME IX requirements.

BR
Deerendra

--

Navanath Kashid

unread,
Feb 16, 2025, 1:49:53 AMFeb 16
to material...@googlegroups.com
image.png
With attached code ref. you can use EN ISO 15614-1 WPQR test results for preparation of WPS/PQR as per ASME BPVC Sec. IX.
Thanks.

       Best Regards,
       Navanath Kashid
       International Welding Engineer (IWE-IIW)
       Mob. No. 9665851969


On Sat, Feb 15, 2025 at 6:05 PM <material...@googlegroups.com> wrote:

Can anybody suggest if we can prepare a asme ix wps based on the test
carried out as per iso 15614-1?
 
venkateswara reddy Desireddy <dvre...@gmail.com>: Feb 15 01:23PM +0530

Both codes are not identical,
Both codes having separate formats. Mechanical testings tensile and bend
test same for both codes. So after testing you can write WPS for ASME and
PED separate.
 
Regards
D.V.Reddy
 