suitables electrode used for cast iron

[izzuddin mustafa]

Hi experts, I need your help. I prepared procedure to welding panama chock (cast iron material)  to high tensile strength plate (EH 36). what is the suitable eloctrode to used for smaw process? can i used the  ordinary low hidrogen eloctrode such as KOBE brand E 7018? or special elctrode? please advice me. Thank you. Ezzudine Must.

[Jim Nystrom]

Rockmount by far has the best products I have ever used for cast iron, and have a rod for all welding techniques.

http://www.weldit.com/product1.html

 

 

Best Regards,

 

Jim Nystrom

jnys...@campbellap.com -

 

P  Please consider the environment before printing this e-mail

--
To post to this group, send email to material...@googlegroups.com
To unsubscribe from this group, send email to materials-weld...@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

[J.Suryanarayanan]

U can use

 

1)  EutecTrode 27 for Base layer

 

2)  Xuper 2240 for final layer

 

with best rgds

= s p raman=

 

----- Original Message -----

 

 

From: izzuddin mustafa

To: materials-welding Group

Sent: Tuesday, April 17, 2012 3:09 PM

Subject: [MW:14117] suitables electrode used for cast iron

--

[Engr huzaifa shabbir]

DEAR FRIEND,
IF YOU USED LOW HYDROGEN ELECTRODE FOR CAST FE 7& HIGH STRENGTH MATERIAL, THE WELD WILL CRACK OR MAY CRACK IN FUTURE
THE MOST SUITABLE ELECTRODE FOR THIS TYPE OF JOINTS IS ANY HIGH PERCENT NICKEL ELECTRODE.
FOR ANY QUERY U MAY CALL +923312041785
OR CONTACT ON engr.h...@gmail.com

REGARDS
HUZAIFA
QA/QC ENGR
PEOPLE STEEL MILLS KHI

--

[Karthik]

Hi,

Please find herewith the attached file might be useful to you. You should use NiFe based electrodes for SMAW welding (AWS A5.15 ENiFe-CI)

 

Thanks & Regards,

(Karthik)

Karthikeyan.S

QA/QC Manager

German-Thai Boiler Engineering Cooperation Limited.

Rayong Factory ;

379 Moo.6 Soi 8, Tambol Pananikom,

Nikompattana, Rayong 21180 THAILAND

Tel : +66 38 897 035-9 Ext. 137

Fax : +66 38 897 034

Hand Phone: 0066 892512282

---

From: Engr huzaifa shabbir <engr.h...@gmail.com>
To: material...@googlegroups.com
Sent: Thursday, April 19, 2012 1:38 PM
Subject: Re: [MW:14127] suitables electrode used for cast iron

[Maulik Thakkar]

Dear all,

I think the question is wrong. Panama chock always made by cast steel rather by cast iron!!

Please understand difference between cast steel and cast iron!!!

Dear huzaifa please check your material of panama chock again


Regards,
Maulik Thakkar
Welding Engineer
L & T limited, Hazira

[Maulik Thakkar]

If panama chock is of cast steel than you can use E7018 electrode.

Regards,

Maulik

[Roy Liu]

Hi, Ezzudine Must

you can not use mild steel to weld Dissimilar steels. crack!!!

You know Cast Iron is too difficult to be welded, so in this case, you have two choices.

1, cast iron electrode: ENi-C1

2, Nickel base material: ENiCrFe-3   (wire:ERNiCr-3)

 

Please find enclosed sheets.

 

any question, please contact me.

 

Roy  from Boehler Welding

To unsubscribe from this group, send email to mailto:materials-welding%2Bunsu...@googlegroups.com

For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to material...@googlegroups.com

To unsubscribe from this group, send email to mailto:materials-welding%2Bunsu...@googlegroups.com

For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to material...@googlegroups.com

To unsubscribe from this group, send email to mailto:materials-welding%2Bunsu...@googlegroups.com

For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

[kannayeram gnanapandithan]

ENiCrFe3 or ERNiCr3 are not atall used for cast iron welding
Only ENi-CI or ENiFe-CI are widely used for cast iron welding
There are best electrodes are available with L&T-EWAC alooys like 224/2204
Pandithan
In-Charge/Welding Technology
Cethar Ltd

> ------------------------------------------------------------------------------