[Mohamed Elsayed]

Hello dears

I'm going to weld SA-240 310s (P.no8) to SA-213 T11 (P.no4), but I don't know what is the proper electrod or filler metal to weld this material, so help me please

[Ahmed Osman]

* if PWHT is needed for 213 T11  ... cladding technique will be used ( 1st clad P4 with ERNiCr-3 then finalize PWHT ) (2nd weld with P8 with same electrode )

* If PWHT not needed for 213 T11 and

   - service temp. less 315c     -- use 309L

   - service temp. more 315C  -- go with ERNiCr-3

best regards

Ahmed Osman

On Monday, August 14, 2023 at 02:26:15 p.m. GMT+3, Mohamed Elsayed <m.say...@gmail.com> wrote:

Hello dears

I'm going to weld SA-240 310s (P.no8) to SA-213 T11 (P.no4), but I don't know what is the proper electrod or filler metal to weld this material, so help me please

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAKujbmu2ZYjN8UsS-ko2PZu0YT1EUHFBV1JPHM8ZdNvRP65E_Q%40mail.gmail.com.

[manish kulkarni]

Pl refer API RP 582 

Sent from Yahoo Mail for iPhone

On Monday, August 14, 2023, 3:26 PM, Mohamed Elsayed <m.say...@gmail.com> wrote:

Hello dears

I'm going to weld SA-240 310s (P.no8) to SA-213 T11 (P.no4), but I don't know what is the proper electrod or filler metal to weld this material, so help me please

--

[Kannayeram Gnanapandithan]

what is the thickness. 

If Thickness is less than 13mm, Preheat T11 side and weld T11 + ASS with ER NiCr3

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/440702323.980444.1692078418046%40mail.yahoo.com.