[williams p wilson]

Dear Experts,

QW-407.2 is not applicable when an impact test is required, Please confirm.

Thank You & Regards

Williams P Wilson

QA/QC Engineer

Please consider the environment before printing this message

[Manikandan J]

Hai,

QW407.2 is a supplementary essential variable.

 Not applicable when an impact test is required

Regards,

Manikandan

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAHBxnQ5oT-m79w8dV_Bjeruvu5qfTPzyY4ouu9Uy%2BaZ5fd76mA%40mail.gmail.com.

[Pravin Kurade]

Supplement variable applicable when impact required

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPdGVmOCoytFUncdCBhgxta4NayXjRQWA6pseH79B%2Br1qo0-mw%40mail.gmail.com.

--

Pravinkumar kurade

[Kannayeram Gnanapandithan]

1. QW407.2 is the supplementary essential variable.  This applicable when impact is required. Before carrying out the PQR, u have to calculate the what is the maximum base metal /weld metal thickness expected in Production, based on this, PQR should undergo minimum 80% time cycle of the production base metal , otherwise new pqr is to be done

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

--

[Kannayeram Gnanapandithan]

supplementary essential-- Then what is the purpose??

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPdGVmOCoytFUncdCBhgxta4NayXjRQWA6pseH79B%2Br1qo0-mw%40mail.gmail.com.

[williams p wilson]

Dear Sir,

My case is note below FYR,

MOC : SA 516 Gr.70 N, 70 mm Thickness

Design Temperature : -28 to 121.11 degree c, Impact Test is required as per UCS-66 Curve D

PWHT (Temp: 595 Degree C Minimum, Holding Time : 2 x 132 Minutes ( Fab. + Future Service Repair)

As you said in the email below , Can I qualify the PQR with 595 Degree C Min. with a holding time of 211.20 minutes.

Please confirm - Thanks in advance.

Thank You & Regards

Williams P Wilson

QA/QC Engineer

Please consider the environment before printing this message

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eMRorvGf6w6VSuwqpGT-c-HFmT-u2rLHnCOVZYuu47%3DyQ%40mail.gmail.com.