Reinforcement pad requirements

[Manish Kumar]

Hi, 

Please share the selection criteria about the requirements of reinforcement pad of pipe. 

Thanks

Regards

Manish Kumar

Inspection(Mechanical) Engineer

[Tajuddin Mohammed]

as per 01-SAMSS-010 para 5.5 Reinforcing and Attachments
Steel plate used for reinforcing pads, sleeves, saddles and other structural
attachments shall conform to a code listed plate material with specified
minimum yield strength of 241.3 MPa (35,000 psi) or greater, depending on
design requirements.
All reinforcing and attachment welds shall be continuous. Skip or stitch
welding is not permitted

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAHfQ4k5kqrtdmDSotHHzH2%2B5yS75a9zOJ6O7cPjtS3YnzFBYbg%40mail.gmail.com.

--

Thanks & Regards

Mohammed Tajuddin

WELDING INSPECTOR CSWIP 3.1

Contact  0530833486

JUBAIL

[Pravin Kurade]

Hello 

Refer UG 36(c) if openings meet the requirements them RF pad not required. 

However if the above conditions doesn't Meet then need to provide RF pad as per UG-37.

You have to provide additional area based on area removed. 

Thanks with Regards....

Pravinkumar Kurade

ASME Authorized Inspector (National Board-15396), 

Repair Inspector (NBIC) R-Endorsement,

PED Inspector, DOSH Inspector,

B.E. (Mech.), Lean Six Sigma Green Belt,

C-SWIP-3.1 (Welding Inspector - UK)

ASNT Level II - MT, PT, RT , VT, LT

Mob : +91 8484848029

[Manish Kumar]

Hi, 

Please share the information about reinforcement pad requirements against the ASME B31.3

Regards

Manish Kumar

Inspection(Mechanical) Engineer