FW: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
pgoswami
Elshan,
It’s very difficult to get information on steels of ABS specifications as they’re proprietary. However I dug out these information. Let me know if your project involves:-
· The same ABS specifications
· Is it the same AH36 material, you’re talking about.
· Would it be convenient from your end to email the applicable part/portions of ABS specs.
I am asking the above in order to make sure that I would be able to advice on the correct spec and materials.
Thanks.
Pradip Goswami,P.Eng.
Welding & Metallurgical Engineer/Specialist
Ontario Power Generation Inc.
Email-pgoswami@sympatico.ca,
From: Elshan
Feyzullayev [mailto:elsh...@hotmail.com]
Sent: Monday, July 12, 2010
1:12 AM
To: pgos...@quickclic.net
Subject: RE: ASTM
A106/API5L X 52 pipe to use instead ABS AH36/dh36
Hi
Pradip,
No it is not resolved yet. Could you please advise? And I
would like to know what is the role of yield strength on structural and
piping construction?
many thanks in
advance.
Elshan.
From:
pgos...@quickclic.net
To: elsh...@hotmail.com
Subject: RE: ASTM
A106/API5L X 52 pipe to use instead ABS AH36/dh36
Date: Sun, 11 Jul 2010
22:15:35 -0400
Hi Elshan,
I missed your email. Is this problem resolved, if not I can dig out the information for you.
Appreciate your response.
Thanks
Pradip Goswami,P.Eng.
Welding & Metallurgical Engineer/Specialist
Ontario Power Generation Inc.
Email-pgoswami@sympatico.ca,
From: Elshan
Feyzullayev [mailto:elsh...@hotmail.com]
Sent: Tuesday, June 08,
2010 12:44 AM
To: pgos...@quickclic.net
Subject: ASTM
A106/API5L X 52 pipe to use instead ABS AH36/dh36
Dear
Pradip,
I
have got the project here a fabrication of the structural platform. The pipe
supports are required to be ABS AH36/DH 36 which is minimum yield strength is
required to be 355 MpA.
Can we substitute this structural
pipe with ASTM A106 Gr B/ASTM A333/API 5L X52 pipe?
Could
you please be so kind to give me a detailed information about
it?
Thank you in advance.
Best regards,
Elshan
Feyzullayev.
Baku, azerbaijan.
Hotmail: Free, trusted and rich email service. Get it now.
Your E-mail and More On-the-Go. Get Windows Live Hotmail Free. Sign up now.
THIS MESSAGE IS ONLY INTENDED FOR THE USE OF THE INTENDED RECIPIENT(S) AND MAY CONTAIN INFORMATION THAT IS PRIVILEGED, PROPRIETARY AND/OR CONFIDENTIAL. If you are not the intended recipient, you are hereby notified that any review, retransmission, dissemination, distribution, copying, conversion to hard copy or other use of this communication is strictly prohibited. If you are not the intended recipient and have received this message in error, please notify me by return e-mail and delete this message from your system. Ontario Power Generation Inc.
Elshan Feyzullayev
This is exactly the same material that you have attached.
It is evident that AH/DH36 has min yield strength 355 mpa. But ASTM A106/API x52 has min yield strength 240 mpa. Therofore ASTM A106/ API X52 can not substitute AH/DH 36.
What role does yield strentgh play in the structural construction then?
best regards,
From: pgos...@quickclic.net
To: material...@googlegroups.com
Subject: [MW:5956] FW: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
Date: Mon, 12 Jul 2010 19:19:02 -0400
--
To post to this group, send email to material...@googlegroups.com
To unsubscribe from this group, send email to materials-weld...@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
Hotmail: Trusted email with powerful SPAM protection. Sign up now.
Vinod Upadhyay
israr
As per my experience thease ABS grade materials are for plate, for
Pipe you can use API 5L Ge X 52Z SR 18,
If pipe is fabricated by plate u can use EN 10025 S 355 K2G3 Material.
On Jul 13, 4:19 am, "pgoswami" <pgosw...@quickclic.net> wrote:
> Elshan,
>
> It's very difficult to get information on steels of ABS specifications as
> they're proprietary. However I dug out these information. Let me know if
> your project involves:-
>
>
> . Is it the same AH36 material, you're talking about.
>
> . Would it be convenient from your end to email the applicable
>
> I am asking the above in order to make sure that I would be able to advice
> on the correct spec and materials.
>
> Thanks.
>
> Pradip Goswami,P.Eng.
>
> Welding & Metallurgical Engineer/Specialist
>
> Ontario Power Generation Inc.
>
>
> pgosw...@quickclic.net
> From: Elshan Feyzullayev [mailto:elsha...@hotmail.com]
> Sent: Monday, July 12, 2010 1:12 AM
> To: pgosw...@quickclic.net
> Subject: RE: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
>
> Hi Pradip,
>
> No it is not resolved yet. Could you please advise? And I would like to know
> what is the role of yield strength on structural and piping construction?
>
> many thanks in advance.
>
> Elshan.
>
> _____
>
> To: elsha...@hotmail.com
> Subject: RE: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
> Date: Sun, 11 Jul 2010 22:15:35 -0400
>
> Hi Elshan,
>
> I missed your email. Is this problem resolved, if not I can dig out the
> information for you.
>
> Appreciate your response.
>
> Thanks
>
> Pradip Goswami,P.Eng.
>
> Welding & Metallurgical Engineer/Specialist
>
> Ontario Power Generation Inc.
>
>
> pgosw...@quickclic.net
>
> _____
> From: Elshan Feyzullayev [mailto:elsha...@hotmail.com]
> Sent: Tuesday, June 08, 2010 12:44 AM
> To: pgosw...@quickclic.net
> Subject: ASTM A106/API5L X 52 pipe to use instead ABS AH36/dh36
>
> Dear Pradip,
>
> I have got the project here a fabrication of the structural platform. The
> pipe supports are required to be ABS AH36/DH 36 which is minimum yield
> strength is required to be 355 MpA.
>
> Can we substitute this structural pipe with ASTM A106 Gr B/ASTM A333/API 5L
> X52 pipe?
>
> Could you please be so kind to give me a detailed information about it?
>
> Thank you in advance.
>
> Best regards,
> Elshan Feyzullayev.
> Baku, azerbaijan.
>
> _____
>
>
> _____
> Your E-mail and More On-the-Go. Get Windows Live Hotmail Free. Sign up now.
>
> _____
> THIS MESSAGE IS ONLY INTENDED FOR THE USE OF THE INTENDED RECIPIENT(S) AND
> MAY CONTAIN INFORMATION THAT IS PRIVILEGED, PROPRIETARY AND/OR CONFIDENTIAL.
> If you are not the intended recipient, you are hereby notified that any
> review, retransmission, dissemination, distribution, copying, conversion to
> hard copy or other use of this communication is strictly prohibited. If you
> are not the intended recipient and have received this message in error,
> please notify me by return e-mail and delete this message from your system.
> Ontario Power Generation Inc.
>
> 183KViewDownload