wall thickness tolerance

[Alix]

Dear All,

I have the following issue concerning the wall thickness tolerance in API 5L.

 

As I understood, this tolerance is related to the manufactured pipe and not the steel plate (e.g. plates used for LSAW line pipes).

 In other words, if the wall thickness of the required pipe is to be 14.3 mm, can we use a plate of 13.8 mm thickness to produce it or the thickness should be 14.3mm at least? 

  

It would be very helpful if you can explain this case or advise me for some references.

Best regards 

[pradip kumar Sil]

 10% bilateral  tolerance is acceptable

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/ca04931d-ffb0-45b5-a12e-31d754a529e5%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.