Dear Experts,  

Impact testing requirements for  Equipment Anchor Chair to top plate/wash welding, base plate, and plug welding.
According to ASME B31.3  above 25mm impact test required.
So for that,  I have restricted to my thickness range 5.00mm to 25.4 mm in WPS.
But Now my requirements for welding Equipment Anchor Chair to top plate/wash welding, base plate, and plug welding.  up to  32.88 mm,
For the 32.88 mm thickness, I have to conduct an impact test or not required impact test 
Process - SMAW.
P No - P1.Gr.No- 1 to P1 Gr,1/2
Thickness range - 5.00 mm to 32.88 mm.
Material - ASTM 516 Gr.60 to ASTM Gr.70

As per ASME Sec IX Ed. 2019, ASME Sec VIII, Div-1, and API RP 582according to mentioned code required Impact test or not?

Thanks in advance  

Regards
KK





harenath jha

unread,
Aug 26, 2020, 2:10:31 AM8/26/20
to material...@googlegroups.com
Impact testing is very much required.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/b8875b6c-08f8-4701-9b20-518206a2b1een%40googlegroups.com.

K K

unread,
Aug 28, 2020, 7:05:40 AM8/28/20
to Materials & Welding
 Dear Experts,  
  
Can I get a response from you?

According to  ASME Sec.8, and MDMT is 5°C.

Please send me your valuable reply to my doubts.

Thanks and Regards
KK

pgos...@rogers.com

unread,
Aug 28, 2020, 8:47:34 AM8/28/20
to material...@googlegroups.com

Hi KK,

 

What’s the design  code ? ASME Sec VIII , DIV-1 or ASME B-31.3. Looking at the text below, it sounds  Sec VIII, DIV-1 is the design code.

Look at this curve and the exemption clauses for more clarifications. If this curve exempts BM/thickness from impact test , then weld/HAZ should be exempted from impact also.

 

Thanks.

 

 

Pradip Goswami, P.Eng, IWE

Consultant-Welding-Metallurgical Engineering

 

Cell & Whatsapp-905-9793232.

Personal:pgos...@rogers.com

 

 

--

https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.

image002.png

Vinoth Rajendran

unread,
Aug 28, 2020, 11:45:33 AM8/28/20
to material...@googlegroups.com

Customer Care

unread,
Aug 28, 2020, 11:33:45 PM8/28/20
to material...@googlegroups.com

Hello,

You would almost certainly have to go Charpy impact  test for 32.88mm thickness and MDMT 5 Centigrade.

It is per UCS 66 (a) ASME Section VIII, Div. 1. Combining thickness, temperature and materials (SA 516 Gr 60 / SA 516 Gr.70), you would be slightly below curve B of Fig. UCS 66 M.

This, for the WPS with this combination of base materials.

 

Anyway, recheck the final thickness. And compare with the data given by the Curve.

 

It is also possible that my assessment is wrong. It's a matter of reading what the experts have already told you.

 

Ramon Briceno

 

Sent from Mail for Windows 10

Kiran Ekbote

unread,
Aug 28, 2020, 11:33:45 PM8/28/20
to material...@googlegroups.com
ASME Sec IX Ed. 2019, ASME Sec VIII, Div-1, and API RP 582

Thank you very much for your response.



--

KIRAN

Vinay Thattey

unread,
Aug 30, 2020, 11:35:59 AM8/30/20
to material...@googlegroups.com
DEAR ;

IN MY VIEW IT IS REQUIRED.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
Reply all
Reply to author
Forward
0 new messages