Dish End Spin Hole Block

[Rahul Chaudhari]

Dear All, 

Greetings.

WE have manufactured 10% torispherical dish end in house & block dish ends spin hole as per attached photographs. 

Please kindly advise me, is it acceptable as per good engineering practice or not?

Material IS IS2062. Thickness is 10mm. Job - horizontal storage tank

Thanks & Regards,

Rahul Chaudhari
+918149199922

[Chiranjeevi A]

Dear Rahul,

Not acceptable

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAHjJ0V9Dy0ZrYO60YQkbyXXwHaNkqB8AkXreW-ZM_fc75oqVBA%40mail.gmail.com.

[Vishwas Keskar]

What was joint design?

Is that joint is made full penetration ?

What NDT was followed ?

Pl send details 

--

[sushil gaur]

Hole is accepted as per ASME sec viii. But you have to make "v" On hole and than patch. Also patch should be radiography examination.. 

Thanks & Regards

Sushil Gaur. 

M. No. 9530278378

--