Dear Sir,

               Please give information about ER 6010 electrode is need baking or holding in portable oven for the root welding of ERW pipes having thickness range 3 to 8 mm.

Please give suggestions.

Thanks and regards

Vishal kumar

Mechanical Engg.

[Bestun Ahmed]

Hi brother, 

No, no need to hold it or keep it in the oven.

Thanks

Bestoon

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAF6t408Ks6qVdKS5qRuS06scPKDDzchmwsx01G20H3kb7Z71Tg%40mail.gmail.com.

[Babur Khan]

Greetings,

Mr. Vishal, E6010 not require any backing or heating due to cellulosic flux.

Best Regards,

Muhammad Babur Khan Lashari

Mechanical Inspector ( Piping / Welding)

Inspection Department
Mob: +966 58 2774568 / 55 968 0573

          +92 334 6186285

Applus Velosi Saudi Arabia

Please consider the environment before printing this e-mail

On Tue, Nov 15, 2022 at 8:26 AM Vishal Jaiswal <vis469j...@gmail.com> wrote:

--

[Muhammad Azeem]

These electrodes are non low hydrogen electrodes which does not required baking before welding , Only need to keep in dry environment and used for downhill welding process. 

Regards,

Muhammad Azeem Iqbal

Welding Inspector Aramco Approved

053110-8577/0554453626/0590071467

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CANd6T%2B_vDKQpAqGfCGt90zB_BW8jYs1%3Drs4Qx7gHiSyC24uxgQ%40mail.gmail.com.

[Kannayeram Gnanapandithan]

6010 doesn't required baking because it is being designed to have more ammount of Hydrogen around 60ml to give better penetration in cross country pipe. Hydrogen is being a non conductivity , it does not allow electric arc to flow smoothly, so more arc force is required to push the current which in tern gives deeper penetration.   IF U DO BAKING, HYDROGEN WILL GET VANISHED

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAHqH7yDQw7_MLGTgoE_DX4cXcNF%2Bh7W4_PVxSVbRC-8qMF3KNA%40mail.gmail.com.

[Vishal Jaiswal]

Dear All,

 Please suggest ,which welding is sutaible for cable tray joint used in PEB Shade.

[Ritesh Kumar Singh]

You can use E 6013 .

On Fri, 18 Nov 2022, 1:55 PM Vishal Jaiswal <vis469j...@gmail.com> wrote:

Dear All,

 Please suggest ,which welding is sutaible for cable tray joint used in PEB Shade.

--

https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAF6t40_evtAiirxMnqGjYe6uo0a87cGzJW6qxV24suVxZFL8ow%40mail.gmail.com.

[Vishal Jaiswal]

Dear all 

What is basic inspection for stud weldind and for welder also

[james gerald]

Check ASME Sec.IX

On Friday, 18 November, 2022 at 04:43:16 pm IST, Vishal Jaiswal <vis469j...@gmail.com> wrote:

Dear all 

What is basic inspection for stud weldind and for welder also

--

https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAF6t4080bnsCbpOgkeDMhjop6cTQYboeGLD4fPX-ZVPVtnTkag%40mail.gmail.com.

[Vishal Jaiswal]

Dear All, 

Please suggest wihich welding is sutaible for GI flat bar to GI flat bar  used in cable tray and also which WPS is use for 

[Kannayeram Gnanapandithan]

7018

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

On Mon, Nov 21, 2022 at 9:18 AM Vishal Jaiswal <vis469j...@gmail.com> wrote:

Dear All, 

Please suggest wihich welding is sutaible for GI flat bar to GI flat bar  used in cable tray and also which WPS is use for 

--

https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAF6t40-BfGWU15koamWdVZ4NsvN_v7mgs69dDW0V6BE%2BUSHqDA%40mail.gmail.com.

[ahmed adil]

Dear Vishal

Oxyacetylene welding or Thermit welding are suitable for your job

Best wishes

Ahmed Adil

Welding engineer 

On Mon, 21 Nov 2022, 06:48 Vishal Jaiswal, <vis469j...@gmail.com> wrote:

Dear All, 

Please suggest wihich welding is sutaible for GI flat bar to GI flat bar  used in cable tray and also which WPS is use for 

--

[Vishwas Keskar]

E6010 is best rod for GI trays

Sent from my iPhone

On 22-Nov-2022, at 1:44 PM, ahmed adil <ahmed.a...@gmail.com> wrote:



To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPZgYYx55KmdEzhaTv5xYSxHGF0zirQia1FXbuFowy%3DSRmpS-g%40mail.gmail.com.

[Gopi Krishna Banerjee]

SMAW with E 7018 electrode Or  CO2 Welding.

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPZgYYx55KmdEzhaTv5xYSxHGF0zirQia1FXbuFowy%3DSRmpS-g%40mail.gmail.com.

[Student]

6010 is good for galvanized steel. But make sure to clen the joint area of zinc coating before welding, since zinc vapours are health hazard