Re: [MW:24334] Failure Analysis // failure during Hydrotesting

[Raghuram Bathula]

few of them could be Material itself, cracks arising out airstrikes or during fabrication, hydrotest temperature etc. refer below link

http://products.asminternational.org/fach/data/fullDisplay.do?database=faco&record=961&trim=false

On 21 February 2016 at 12:51, 'Shashank Vagal' via Materials & Welding <material...@googlegroups.com> wrote:

Dear all,

Please suggest what could have caused this pipe failure after Hydrotesting..... Consider all general conditions as all details are not known yet

 

BR,

Shashank C Vagal 

[Shashank Vagal]

Thanks, it is very useful.

 

BR,

Shashank C Vagal 

---

From: Raghuram Bathula <raghura...@gmail.com>
To: Materials-Welding <material...@googlegroups.com>
Sent: Sunday, 21 February 2016 3:20 PM
Subject: Re: [MW:24335] Failure Analysis // failure during Hydrotesting

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To post to this group, send email to material...@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADxVub%3D95qOYzcrJcn-ZNSjn-ukjDrTRZO3qrby9oJxE0MtBDA%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.