Dear Experts
During visual inspection of dish-end (MOC SA 240 Gr304 & Thickness 8mm) I found that heavy dent marks on knuckle area and this may be during forming process. Kindly suggest whether it is allowed as per code to repair by welding on damaged area for such surface defects.
Regards
Amit
A dent in material formation is not a welding defect. Can you include a photo. A weld repair is exactly that! A repair to the welded area. Otherwise it is a fabrication repair. Please clarify
--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To post to this group, send email to material...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAOi%3DZp-ruFFWNikVwjAn0FwHVrD3WQyKJ8Qs1rSCr1mEt%2BLbig%40mail.gmail.com.
Hi!Basicaly before forming of DE you require to consider the reduction in wall thk in knuckle portion and accordigly you req to select higher thk. Plate for DE As this forming is carried by point pressing and followed by leveling or say dressing the surface by pressing to level dents (to maintain min req wall thk )Dents are not acceptable and not to be repaired by welding for thk correctionTherefore one has to be careful during DE forming with due consideration to Die its surface n shape used and pressure appliedRegards
On Mon, 24 Apr 2017 at 17:14, anthony chundal<anthony...@gmail.com> wrote:
you can repair the same, provided you have a repair procedure,& a suitable Welding procedure. what is the minimum thickness required after forming,whether you are achieving the same before repair.
On Sun, Apr 23, 2017 at 5:44 PM, claire roberston <jamis...@hotmail.co.uk> wrote:
A dent in material formation is not a welding defect. Can you include a photo. A weld repair is exactly that! A repair to the welded area. Otherwise it is a fabrication repair. Please clarify
--
http://www.linkedin.com/ groups/MaterialsWelding- 122787?home=&gid=122787&trk= anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@ googlegroups.com.
To post to this group, send email to material...@ googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/ msgid/materials-welding/ cc4538ad-966e-4e19-9b86- 5cafe3318697%40googlegroups. com.
For more options, visit https://groups.google.com/d/ optout.