Regarding welding of ErNicr3 and PWHT

Anuj Sharma

unread,

Apr 12, 2016, 10:14:31 AM4/12/16

to Materials & Welding

Hi everyone please suggest

We have very less constrained space for the PWHT on and we have called 4 different PWHT teams and all teams have ignored PWHT due to less space.
Our material is SSH Header 40 mm thick and P91 material ehich we have to dummy with P91 material only.
As recommended by us to use ErNiCr3 filler wire with pre heat at 220deg C and no PWHT required is it ok.
??

Vishwas Keskar Welding Manager Pune India

unread,

Apr 17, 2016, 11:05:56 AM4/17/16

to Materials & Welding

Pl. carry out PWHT. Though Ni based consumables is used, weld may be softer but the HAZ is too hard and very less ductility . So may crack when pressure (in service) is applied.

Kannayeram Gnanapandithan

unread,

Apr 18, 2016, 1:24:40 AM4/18/16

to materials-welding

U can not avoid pwht on P91 inspite nickel base electrode used,but u can reduce the pwht temp

--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To post to this group, send email to material...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/2ede58fd-ff14-4642-9f4f-be9425e26295%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

Vishwas Keskar Welding Manager Pune India

unread,

Apr 24, 2016, 11:50:43 PM4/24/16

to Materials & Welding

PWHT is must in view of Hard HAZ on GR 91 side

On Tuesday, April 12, 2016 at 7:44:31 PM UTC+5:30, Anuj Sharma wrote: